321 309S 301 Stainless Steel Strip For Springs Polished Thin

Place of Origin Made in China
Brand Name Vespolari Jiangsu
Certification ISO SGS ROHS
Minimum Order Quantity 1Ton
Price Negotiable
Packaging Details standard waterproof package
Delivery Time 7-14 business days
Payment Terms TT L/C
Supply Ability 10000000per month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Name Stainless Steel Coil/Strip Material 201/304/304L/321/316/316L/309/309S/310S/904Lect, Or Customized
Thickness 0.17 Mm~3 Mm Width 10 Mm~250 Mm
Standard ASTM, JIS, GB, AISI, DIN, BS,EN Certificate ISO
High Light

321 stainless steel strip

,

stainless steel strip polished

,

thin stainless steel strips

Leave a Message
Product Description

309(S) stainless steel coil

Types 309 Stainless Steel and 309S are austenitic chromium-nickel stainless steels that provide excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures.

Online consultation

Project Introduction

Types 309 Stainless Steeland 309S are austenitic chromium-nickel stainless steels that provide excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. Type 309S Stainless Steelis identical to Type 309 except for a lower carbon content that minimizes carbide precipitation and improves weldability. They are essentially nonmagnetic as annealed and become lightly magnetic when cold worked.

Specifications

ASTM A167 (309), ASTM A240 (309S)

Typical Applications

furnace parts, heating elements, aircraft and jet engine parts, heat exchangers, sulfite liquor handling equipment, kiln liners, boiler baffles, refinery and chemical processing equipment, and auto exhaust parts.

Chemical Composition: (A167, A240)

Element

Type309

Type309S

Carbon

0.20 max.

0.08 max.

Manganese

2.00 max.

2.00 max.

Sulfur

0.030 max.

0.030 max.

Phosphorus

0.045 max.

0.045 max.

Silicon

0.75 max.

1.0max.

Chromium

22.0 24.0

22.0 24.0

Nickel

12.0 15.0

12.0 15.0

Mechanical Properties: (ASTM A167, A240)

Type

Yield Strength 0.2% offset (KSI)

Tensile Strength (KSI)

% Elongation (2" Gauge length)

Hardness Rockwell

309

30 min.

75 min.

40 min.

HRB 95 max.

309S

30 min.

75 min.

40 min.

HRB 95 max.

Physical Properties

Density (lb./ in^2) @ RT

 

0.29

Modulus of Elasticity in Tension (psi x 10^6)

 

29.0

Specific Heat (BTU/°F/lb.)

32 to 212 °F

0.12

Thermal Conductivity (BTU/hr/ft^2/ft)

212°F

9.0

 

932°F

10.8

Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F)

32 to 212°F

8.3

 

32 to 600°F

9.3

 

32 to 1,000°F

9.6

 

32 to 1,200°F

10.0

Electrical Resistivity (micro ohms - cm)

at 70°F

39.8

Melting Point Range (°F)

 

2550 - 2650

Oxidation Resistance - Continuous Service(°F)

 

2000

Oxidation Resistance - Intermittent Service(°F)

 

1800

Processing

These alloys are not hardenable by heat treatment. Anneal at 1900 - 2050°F (1038 - 1121°C), then water quench or rapidly air cool.

Forming

Types 309 and 309S Stainless Steels can be roll formed, stamped and drawn readily. In-process annealing is usually required to reduce hardness and increase ductility.

Welding

Type 309 is generally considered to have weldability nearly equivalent to the most common alloys of this class, Types 304 and 304L. When a weld filler is needed, AWS E/ER 309 and 310 are most often specified.

Corrosion

Types 309 and 309S provide excellent general corrosion resistance. They are more resistant to marine atmospheres than Type 304. They exhibit high resistance to sulfite liquors and are useful for handling nitric acid, nitric-sulfuric acid mixtures, and acetic, citric, and lactic acids.