304 304L Stainless Steel Sheet Plate Excellent Corrosion Resistance For Instrumentation
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xName | Stainless Steel Sheet Plate | Type | SS Tube |
---|---|---|---|
Length | 2000/2438/2500/3000/3048 Mm | Width | 1000/1219/1250/1500 Mm |
Processing Service | Bending, Welding, Decoiling, Punching, Cutting | Delivery Time | 7-15 Days |
Surface | BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D | ||
High Light | 304L Stainless Steel Sheet Plate,Instrumentation Stainless Steel Sheet Plate,1000mm stainless steel plate sheet |
Excellent Corrosion Resistance 304 304L Stainless Steel Sheet Plate For Instrumentation
Item
|
stainless steel plate/sheet/coil
|
Grade
|
300/400/600 Series
|
Standard
|
JIS, AiSi, ASTM, GB, DIN, EN
|
Length
|
customized
|
Width
|
customized
|
Place of Origin
|
Shandong
|
Brand Name
|
Linxu
|
Type
|
plate/sheet/coil
|
Tolerance
|
±1%
|
Processing Service
|
Bending, Welding, Decoiling, Punching, Cutting
|
Surface Finish
|
2B
|
Delivery Time
|
10-15 days
|
Chemical Composition
Element |
Type 430 |
Carbon |
0.12 max. |
Manganese |
1.00 max. |
Sulfur |
0.030 max. |
Phosphorus |
0.040 max. |
Silicon |
0.75max. |
Chromium |
16.0 18.0 |
Nickel |
0.60max. |
Mechanical Properties
Type |
Yield Strength 0.2% offset (KSI) |
Tensile Strength (KSI) |
% Elongation (2" Gauge length) |
Hardness Rockwell |
430 Ann |
30 min. |
65 min. |
22 min |
HRB 89 |
Physical Properties
Density (lb./ in^2) @ RT |
0.278 |
|
Modulus of Elasticity in Tension (psi x 10^6) |
29.0 |
|
Specific Heat (BTU/°F/lb.) |
32 to 212 °F |
0.11 |
Thermal Conductivity (BTU/hr/ft^2/ft) |
212°F |
13.8 |
932°F |
15.0 |
|
Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F) |
32 to 212°F |
5.7 |
32 to 932°F |
6.2 |
|
Electrical Resistivity (micro ohms - cm) |
at 70°F |
60.0 |
Melting Point Range (°F) |
2600 - 2750 |
|
Oxidation Resistance - Continuous Service(°F) |
1500 |
Processing
Type 430 should be annealed at 1450-1550F and furnace cooled at a rate of 50°F per hour to 1100°F and air cooled. If the annealing temperature does not exceed 1450°F (790°C), an air cool may be substituted for the furnace cool when annealing thin sections.
Forming
Type 430 is readily drawn and formed. Its drawing characteristics are similar to those of low-carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power.
Welding
Type 430 is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid brittle weld fractures during fabrication. When a weld filler is needed, AWS E/ER 308L and 430 are most often specified. Corrosion: This alloy is resistant to attack in a wide variety of corrosive media including nitric acid, and many organic acids.