201 316l Stainless Steel Strip Trim Transition Adhesive

Place of Origin Made in China
Brand Name Vespolari Jiangsu
Certification ISO SGS ROHS
Minimum Order Quantity 1Ton
Price Negotiable
Packaging Details standard waterproof package
Delivery Time 7-14 business days
Payment Terms TT L/C
Supply Ability 10000000per month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Name Stainless Steel Coil/Strip Material 201/304/304L/321/316/316L/309/309S/310S/904Lect, Or Customized
Thickness 0.17 Mm~3 Mm Width 10 Mm~250 Mm
Standard ASTM, JIS, GB, AISI, DIN, BS,EN Certificate ISO
High Light

stainless steel transition strip

,

stainless steel trim strip

,

stainless steel adhesive strip

Leave a Message
Product Description
201 stainless steel strip
Product Description
Type 201 Stainless Steelis an austenitic chromium-nickel-manganese stainless steel which was developed to conserve nickel. Type 201 is a lower cost alternative to conventional Cr-Ni stainless steels such as 301 and 304.
Contact Us
Product Features

Type 201 Stainless Steelis an austenitic chromium-nickel-manganese stainless steel which was developed to conserve nickel. Type 201 is a lower cost alternative to conventional Cr-Ni stainless steels such as 301 and 304. Nickel is replaced by additions of manganese and nitrogen. It is non-hardenable by thermal treatment, but may be cold worked to high tensile strengths. Type 201 is essentially nonmagnetic in the annealed condition and becomes magnetic when cold worked. Type 201 can be substituted for Type 301 in many applications.

Specifications

ASTM A240, A666

Typical Applications

Typical applications for Types 201 are cookware, hose clamps, piston rings, transit car structural member, transit car roofing/siding, thermal window spacers, air bag containers, and truck trailer posts and door frames.

Chemical Composition

Element

Type 201

Carbon

0.15x

Manganese

5.5 - 7.5

Sulfur

0.03X

Phosphorus

0.060x

Silicon

1.0 x

Chromium

16 - 18

Nickel

0.6-5.5

Nitrogen

0.25x

Mechanical Properties

Type

Yield Strength 0.2% offset (KSI)

Tensile Strength (KSI)

% Elongation(2" Gauge length)

Hardness Rockwell

201 Ann

38 min.

75 min.

40% min.

HRB 95 max.

201 Hard

75 min.

125 min.

25.0 min.

25 32 HRC (typical)

201 Hard

110 min.

150 min.

18.0 min.

32 - 37 HRC (typical)

201 Hard

135 min.

175 min.

12.0 min.

37 41 HRC (typical)

201 Full Hard

145 min.

185 min.

9.0 min.

41 46 HRC (typical)

Physical Properties

Density (lb./ in^2) @ RT

 

0.283

Modulus of Elasticity in Tension (psi x 10^6)

 

28.6

Specific Heat (BTU/°F/lb.)

32 to 212 °F

0.12

Thermal Conductivity (BTU/hr/ft^2/ft)

212°F

9.4

Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F)

32 to 212°F

8.7

 

32 to 600°F

9.7

 

32 to 1,000°F

10.2

Electrical Resistivity (micro ohms - cm)

at 70°F

69

Melting Po