301 302 304 2b Chef Stainless Steel Checkered Sheet Diamond Stainless Checkered Plate

  • 301 302 304 2b Chef Stainless Steel Checkered Sheet Diamond Stainless Checkered Plate
Place of Origin Made in China
Brand Name Vespolari Jiangsu
Certification ISO SGS ROHS
Minimum Order Quantity 1Ton
Price Negotiable
Packaging Details standard waterproof package
Delivery Time 7-14 business days
Payment Terms TT L/C
Supply Ability 10000000per month

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Name Stainless Steel Sheet Plate Type SS Tube
Length 2000/2438/2500/3000/3048 Mm Width 1000/1219/1250/1500 Mm
Processing Service Bending, Welding, Decoiling, Punching, Cutting Delivery Time 7-15 Days
Surface BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D
High Light

stainless steel diamond sheet

,

stainless steel chequered sheets

,

ss checkered sheet
Leave a Message
Product Description

304 ss checkered plate

stainless steel sheet metal, 304 304LStainless Steel Plate /

304Stainless Steel Sheet 201 430 316 904

 

Free samples, Subject to third-party inspection.

factory Standard AISI ASTM hot/cold roll stainless steel plate

Type 304 Stainless Steelis the most widely used of the austenitic (chromium/nickel) stainless steels. In the annealed condition it is essentially non-magnetic and becomes slightly magnetic with the application of cold work.

Online consultation

Project Introduction

Type 304 Stainless Steelis the most widely used of the austenitic (chromium/nickel) stainless steels. In the annealed condition it is essentially non-magnetic and becomes slightly magnetic with the application of cold work. Type 304L Stainless Steelis preferred in welding applications to exclude the formation of chromium carbides during cooling in the heat affected region of the weld. These alloys represent an excellent combination of corrosion resistance and fabricability.

Specifications

Type 304 ASTM A240, ASTM A666, AMS 5513 Type 304L ASTM A240, ASTM A666, AMS 5511

Typical Applications

Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres

Chemical Composition: (Per ASTM A240)

Element

Type 304

Type 304L

Carbon

0.07Max

0.030 Max

Manganese

2.00Max

2.00 Max

Sulfur

0.030 Max

0.030 Max

Phosphorus

0.045 Max

0.045 Max

Silicon

0.75 Max

0.75 Max

Chromium

17.5 to 19.5

18.0 to 20.0

Nickel

8.0 to 10.5

8.0 to 12.0

Nitrogen

0.10 Max

0.10 Max

Mechanical Properties: (Per ASTM A240, A666)

Type

Yield Strength 0.2% offset (KSI)

Tensile Strength (KSI)

% Elongation(2" Gauge length)

Hardness Rockwell

304 Ann

30 min.

75 min.

40 min.

HRB 92 max.

304 Hard

75 min.

125 min.

12 min.

HRC 25-32 (typical)

304 Hard

110 min.

150 min.

7 min.

HRC 32-37(typical)

304L Ann

25 min.

70 min.

40 min.

HRB 92 max.

304L Hard

75 min.

125 min.

12 min.

HRC 25-32 (typical)

304L Hard

110 min.

150 min.

6 min.

HRC 32-37 (typical)

Physical Properties: (annealed)

   

304 & 304L

Density (lb./ in^2) @ RT

  

0.29

Modulus of Elasticity in Tension (psi x 10^6)

  

28.0

Specific Heat (BTU/°F/lb.)

32 to 212 °F

0.12

Thermal Conductivity (BTU/hr/ft^2/ft)

212°F

9.4
 

932°F

12.4

Mean Coefficient of Thermal Expansion (in. x 10^-6 per °F)

32 to 212°F

9.2
 

32 to 600°F

9.9
 

32 to 1,000°F

10.2
 

32 to 1,200°F

10.4

Electrical Resistivity (micro ohms - cm)

at 70°F

72

Melting Point Range (°F)

  

2550 to 2650

Oxidation Resistance - Continuous Service(°F)

  

1,650

Oxidation Resistance - Intermittent Service(°F)

  

1,500

Processing

Types 304 and 304L cannot be hardened by thermal treatment. Annealing: Heat to1850o°F to 2050 °F and cool at sufficiently high rates through 1500°F to 800°F to avoid precipitation of chromium carbides. Stress Relief Annealing: Cold worked parts should be stress relieved at 750°F for to 2 hours